Effect of intra-orifice barriers on the fracture resistance of endodontically treated teeth - an ex-vivo study.

Abstract

INTRODUCTION:

The purpose of this study was to evaluate and compare the fracture resistance of roots obturated with guttapercha using bonded amalgam, GC Light cure GIC (resin modified glass ionomer cement) and Tetric N Flow (flowable hybrid composite) as different intra orifice barriers.

MATERIALS AND METHODS:

Eighty freshly extracted mandibular premolars with straight roots were reduced to 14 mm from the coronal aspect. All canals were enlarged to size 30 and specimens were obturated with gutta percha cones, except for control group specimens the coronal 3 mm of root fillings of all other group specimens were removed with the aid of heated plugger. All samples were randomly divided into 4 groups of 20 specimens each. They were control, Fuji GC LC GIC, Tetric N Flow and Bonded Amalgam. After the placement of the intra orifice barrier materials, specimens stored at 37(o)C and 100% humidity for one week to allow the materials to set completely. After one week, all the groups were subjected to fracture resistance testing by using Universal testing machine.

RESULTS:

Data was analysed for significance by ANOVA (Analysis of variance) and further pair wise comparison was performed by Benferroni test. Level of significance was taken as 0.05. Tetric N Flow group showed better fracture resistance as compared to all other groups and Control group is least among the groups. Fracture resistance of Tetric N Flow compared with bonded amalgam was statistically significant.

CONCLUSION:

Tetric N Flow and Fuji GC LC GIC can be used as intra-orifice barriers with good fracture resistance in endodontically treated teeth.

• Authors: Shaheen Aboobaker, Baiju Gopalan Nair, Rajesh Gopal, Sandeep Jituri, Fazalu Rahman Pothu Veetil
• Journal: Journal of clinical and diagnostic research : JCDR (J Clin Diagn Res) Vol. 9 Issue 2 Pg. ZC17-20 (Feb 2015) ISSN: 2249-782X [Print] India
• PMID: 25859518 (Publication Type: Journal Article)