Currently, there is no regenerative strategy for the spinal cord that is part of clinical standard of core. Current paths usually include combinations of scaffold materials and active molecules. In a recent study, a permanent
dental resin scaffold for treatment of
spinal cord injury was designed. The results from studies on rats were promising. However, for potential clinical use, a biodegradable scaffold material that facilitates
drug delivery and the regeneration of the spinal cord needs to be developed. Also a biodegradable material is expected to allow a better evaluation of the efficacy of the surgical method. In this article, the suitability of hardened
calcium sulfate cement (CSC) for use as degradable spinal cord scaffolds is investigated in bench studies and in vitro studies. Compressive strength, degradation and microstructure, and the loading capability of
heparin-activated
fibroblast growth factor 1 (
FGF1) via soaking were evaluated. The CSC could easily be injected into the scaffold mold and the obtained scaffolds had sufficient strength to endure the loads applied during surgery. When hardened, the CSC formed a porous microstructure suitable for loading of active substances. It was shown that 10 min of
FGF1 soaking was enough to obtain a sustained active
FGF1 release for 20-35 days. The results showed that CSC is a promising material for spinal cord scaffold fabrication, since it is biodegradable, has sufficient strength, and allows loading and controlled release of active
FGF1.