Morphological Evolution and Damping Properties of Dynamically Vulcanized Butyl Rubber/Polypropylene Thermoplastic Elastomers.

Abstract

We successfully prepared butyl rubber (IIR)/polypropylene (PP) thermoplastic vulcanizate (IIR/PP-TPV) for shock-absorption devices by dynamic vulcanization (DV) using octyl-phenolic resin as a vulcanizing agent and studied the morphological evolution and properties during DV. We found that the damping temperature region of the IIR/PP-TPV broadened with the disappearance of the glass transition temperature (Tg) in the PP phase, which is ascribed to the improvement of compatibility between the IIR and PP with increasing DV time. As DV progresses, the size of the dispersed IIR particles and the PP crystalline phase decreases, leading to the formation of a sea-island morphology. After four cycles of recycling, the retention rates of tensile strength and elongation at break of the IIR/PP-TPV reached 88% and 86%, respectively. The size of the IIR cross-linking particles in the IIR/PP-TPV becomes larger after melt recombination, and the continuous PP phase provides excellent recyclability. Significantly, the prepared IIR/PP-TPV exhibits excellent recyclability, high elasticity, and good damping property.

• Authors: Qi Tang, Shiteng Hu, Lijing Han, Chengzhong Zong, Jujie Sun
• Journal: Polymers (Polymers (Basel)) Vol. 14 Issue 13 (Jul 04 2022) ISSN: 2073-4360 [Electronic] Switzerland
• PMID: 35808785 (Publication Type: Journal Article)