A dental composite containing
amorphous calcium phosphate nanoparticles (NACP) was developed that released
calcium (Ca) and
phosphate (PO(4))
ions and possessed
acid-neutralization capability. There has been little study on incorporation of
antibacterial agents into
calcium phosphate composites. The objective of this study was to investigate the effect of
silver nanoparticle (NAg) mass fraction in NACP nanocomposite on mechanical properties and
dental plaque microcosm biofilm for the first time. NACP nanoparticles of 116 nm were synthesized via a spray-drying technique. NAg nanoparticles were synthesized using Ag 2-ethylhexanoate and 2-(tert-butylamino)ethyl
methacrylate, yielding NAg of particle size of 2.7 nm that were well-dispersed in the resin. Five NACP nanocomposites were fabricated with NAg mass fractions of 0, 0.028, 0.042, 0.088, and 0.175%, respectively. Mechanical properties of NACP nanocomposites containing 0-0.042% of NAg matched those of a commercial composite without antibacterial activity. Live/dead assay of
dental plaque microcosm biofilms showed complete coverage with live bacteria on commercial composite. However, there were increasingly more dead bacteria with higher NAg content in the NACP nanocomposite. Colony-forming unit (CFU) counts for total microorganisms, total streptococci, and mutans streptococci for NACP nanocomposite with 0.042% NAg were about 1/4 those of commercial composite.
Lactic acid production on NACP nanocomposite with 0.042% NAg was 1/3 that on commercial composite. In conclusion, novel NACP-NAg nanocomposites were developed which possessed good mechanical properties and potent antibacterial properties, with substantially reduced biofilm viability and
lactic acid production. Hence, the NACP-NAg nanocomposites are promising for dental restorations with remineralizing and antibacterial capabilities.