Abstract |
The aim of the present study was to evaluate the bonding durability of resin-based luting cement to partially stabilized tetragonal zirconia (Y-TZP) achieved by combination treatment of tribochemical (TBC) treatment and two different phosphate acid ester monomers. Two phosphate acid ester monomers (EP: Epricord opaque primer, AZ: AZ primer) were applied to each surface modification followed by application of resin-based luting cement ( Rely-X ARC). Bonding specimens were placed in deionized water at 37 degrees C and stored for 24 h. The other groups were subjected to 30,000 cycles of a thermal stress for the durability test. Shear bond tests were done using a universal testing machine at 1 mm/min. Shear bond strengths of combination treatments using EP and AZ on TBC treatment after thermal stress showed no significant difference (p>0.05) compared with those of storage after 24 h. Combination treatment using phosphoric acid ester monomer could achieve a durable bond.
|
Authors | Kenichiro Takeuchi, Akihiro Fujishima, Atsufumi Manabe, Soichi Kuriyama, Yasuhiro Hotta, Yukimichi Tamaki, Takashi Miyazaki |
Journal | Dental materials journal
(Dent Mater J)
Vol. 29
Issue 3
Pg. 316-23
(May 2010)
ISSN: 0287-4547 [Print] Japan |
PMID | 20484831
(Publication Type: Journal Article)
|
Chemical References |
- 6-methacryloyloxyhexyl phosphonoacetate
- Composite Resins
- Methacrylates
- Organophosphates
- Polymethacrylic Acids
- RelyX ARC
- Resin Cements
- epricord
- yttria stabilized tetragonal zirconia
- Dental Porcelain
- Polyethylene Glycols
- Bisphenol A-Glycidyl Methacrylate
- Yttrium
- Zirconium
- Phosphonoacetic Acid
|
Topics |
- Bisphenol A-Glycidyl Methacrylate
- Composite Resins
- Dental Bonding
- Dental Etching
(methods)
- Dental Porcelain
- Dental Stress Analysis
- Friction
- Materials Testing
- Methacrylates
- Organophosphates
- Phosphonoacetic Acid
(analogs & derivatives)
- Polyethylene Glycols
- Polymethacrylic Acids
- Resin Cements
- Shear Strength
- Yttrium
- Zirconium
|