11/01/1999 - "It was concluded that the experimental sealers KT-308 and ZUT bonded better to bovine dentine than Ketac-Endo, and that the bond of all three GIC sealers was better with the smear layer present."
04/01/2003 - "This in vitro study evaluated the effect of smear layer removal on adhesion to human dentine of Ketac-Endo, Grossman, and Sealer 26 root canal sealers. "
08/01/2002 - "The purpose of this in vitro study was to test the effect of Ketac-Endo (KE) and AH 26 on resistance to root fracture and also to evaluate the effect of smear layer. "
10/01/1995 - "This study compared the sealing ability of Ketac Endo with and without smear layer and Tubli Seal. "
05/01/1998 - "The apical seal exhibited by Ketac-Endo was not significantly different from that provided by zinc oxide-eugenol cement (p > 0.05), regardless of the presence or absence of a smear layer."
|2.||Nonvital Tooth (Endodontically-Treated Teeth)
10/01/1995 - "The purpose of this study was to investigate in vitro the effect of immediate and delayed post space preparation as well as the effect of remained length of gutta-percha on the apical seal of endodontically treated teeth obturated by lateral condensation technique using Ketac-Endo as root canal sealer. "
07/01/2009 - "The present study involved the in vitro comparison of root reinforcing abilities of two sealers, i.e., Ketac-Endo and Acroseal, in endodontically treated teeth in the presence and absence of smear layer. "
|3.||Weight Loss (Weight Reduction)
10/01/2003 - "Sealapex, Aptal-Harz and Ketac Endo had a marked weight loss in all liquids."
10/01/2003 - "Most sealers were of low solubility, although Sealapex, Aptal-Harz and Ketac Endo showed a marked weight loss in all liquids. "
01/01/2000 - "In comparison with other classes of material, Ketac Endo was the least soluble in chloroform and halothane (P < 0.01), with less than 1% weight loss after 10 min exposure to either solvent. "
|5.||epoxy resin AH-26
|6.||Zinc Oxide-Eugenol Cement
|10.||Fuji glass-ionomer lining cement (Fuji I)